| Application |
| ?˜ |
| E316LT is suitable for welding of low carbon 18%Cr-12%Ni-2%Mo stainless steel. |
| ?˜ |
| Characteristics |
| ?˜ |
| (1) E316LT is flux cored wire and designed for all-position welding?˜ |
| (2) It provides the excellent usability with stable arc, less spattering, good bead |
| ?˜appearance, better slag removal, and less quantity of welding fume comparable to |
| ?˜solid wire. |
| (3) Is containing Ferrite of a reasonable quantity and crack-resistance, intergranular corrosion resistance, mechanical properties of weld metal are superior. |
| (4) Shield gas is 100% CO2 or Ar-CO2 gas. |
| ?˜ |
| Note in usage |
| ?˜ |
| (1) The optimum flow of CO2 for Shielding is 20~25Ÿ??/min. |
| (2) Protect the weld with a screen to prevent blowholes caused by wind where the wind |
| ?˜velocity is 2m/sec and more. |
| (3) Keep the distance between tip & base metal at 15~25???. |
| ?˜ |
| Typical chemical composition of weld metal (%)?˜ |
| ?˜ |
| ?˜ |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
FN |
| E316LT |
0.029 |
0.64 |
1.48 |
0.012 |
0.009 |
18.35 |
12.29 |
2.51 |
6 |
| ?˜ |
| Typical mechanical properties of weld metal |
| ?˜ |
| ?˜ |
YP |
TS |
EL |
IV J (kgf-m) |
?˜ |
?˜ |
?˜ |
?˜ |
?˜ |
| N/???(kgf/???) |
N/???(kgf/???) |
(%) |
0Ÿ?? |
?˜ |
?˜ |
?˜ |
?˜ |
?˜ |
| E316LT |
547(55.8) |
594(60.6) |
41.1 |
52(5.3) |
?˜ |
?˜ |
?˜ |
?˜ |
?˜ |
| ?˜ |
| Size & recommended current range (DC+) |
| ?˜ |
| Dia. ???(in) |
Current(A) |
Voltage(V) |
Welding Speed(??�/min) |
?˜ |
?˜ |
?˜ |
?˜ |
?˜ |
?˜ |
| 1.2(0.045) |
150~300 |
24~33 |
20~60 |
?˜ |
?˜ |
?˜ |
?˜ |
?˜ |
?˜ |
| 1.6(1/16) |
200~400 |
24~33 |
20~60 |