| Applications |
| E308LT is suitable for Welding of 18% Cr-8% Ni stainless steel (SUS 308) |
| E308LT is suitable for Welding of low carbon 18% Cr-8% Ni stainless steel |
| (SUS 308L) |
| ?˜ |
| Characteristics |
| (1) E308LT is a flux cored arc welding wire to be used with CO2 & mix gas shielding gas. |
| (2) The weld metals contain optimum FN content in their austenitic structures. |
| ?˜?˜?˜ Therefore, their weldability is excellent with lower crack susceptibility. |
| (3) It provides excellent usability with stable arc, less spattering, good bead appearance. |
| ?˜ |
| Notes on usage |
| (1) Keep the distance between tip & base metal at 15Ÿ?ª20??? |
| (2) The flow rate of shielding gas shall be 20Ÿ?ª25Ÿ??/min. |
| (3) The wire has good tolerance to moisture absorption, but it should not be stored in a place of high humidity for long and should be used as fast as possible after taking out from the package. |
| ?˜ |
| ?˜ |
| Typical chemical composition of weld metal (%)?˜ |
| Product |
C?˜ |
Si?˜ |
Mn?˜ |
P?˜ |
S?˜ |
Ni?˜ |
Cr?˜ |
Mo?˜ |
| Name?˜ |
| E308LT?˜ |
0.033 |
0.72 |
1.21 |
0.025 |
0.012 |
10 |
19.3 |
0.23 |
| ?˜ |
| Typical mechanical properties of weld metal (%)?˜ |
| Product |
YP |
TS |
EL |
IV at 0Ÿ?? |
?˜ |
?˜ |
?˜ |
?˜ |
| name?˜ |
N/???(kgf/???)?˜ |
N/???(kgf/???)?˜ |
(%)?˜ |
J (kgf-m)?˜ |
?˜ |
?˜ |
?˜ |
?˜ |
| E308LT |
407(41.5)?˜ |
550(56)?˜ |
44 |
51(5.2)?˜ |
?˜ |
?˜ |
?˜ |
?˜ |
| ?˜ |
| Size & recommended current range (DC+) |
| Dia. (???)?˜ |
.045" |
1/16" |
?˜ |
?˜ |
?˜ |
?˜ |
?˜ |
| Amp?˜ |
AP |
100Ÿ?ª250?˜ |
200Ÿ?ª350?˜ |