E316L-16 3/32" x 10" 5 lbs Stainless Steel Electrode (5 LBS)
We accept payment by any of the following methods:
PayPal & Credit Card
Your order will be dispatched within 1 working day of receiving payment (Monday-Friday) and you should expect to receive it one or two days after dispatch (for orders sent RM 1st Class).
In the very unlikely event that your item is lost or damaged during post, then WE are responsible and will issue either a full refund or replacement.
If you are not 100% satisfied with your purchase, you can return the product and get a full refund or exchange the product for another one, be it similar or not.
You can return a product for up to 14 days from the date you purchased it.
Any product you return must be in the same condition you received it and in the original packaging. Please keep the receipt.
We supply always very competitive price with high quality products.
2. Large Volume
We keep a lot of inventory. Please call us to get better price if you need large volume of products.
3. Fast shipping
We ship within 1 or 2 days after payments with USPS, Fedex and LTL or FTL serice.
4. Quick response & Responsibility
We answer all questions within a couple of hours in day time and if there is any problem on the products, we always accept the return and credit within 15 days.
Please contact us
Call : 678-691-7495
email : firstname.lastname@example.org
- Brand New European E316L-16 3/32" Welding Rod at Great Price & Quality.
- Good weldibility.
- Well sealed packing from moisture.
- We have other grades and size : E308L-16, E309L-16 & E316L-16 (3/32", 1/8" & 5/32")
|Welding of AISI (SUS) 316L stainless steel.|
|E316L-16 is lime-titania type electrodes for all-position welding.|
|As the weld metal is of austenitic structure containing proper quantity of ferrite crack resistibility is good and usability is also good.|
|As extra-low carbon weld metal can be obtained, intergranular corrosion resistibility is superior to that of E316-16|
|Creep rupture strength is also good.|
|Notes on usage|
|(1) Keep the arc as short as possible and choose the welding current as low as possible|
|(2) Weaving width should be within two and a half times of electrode's diameter.|
|(3) When the electrodes have absorbed moisture, dry them at 250-300??for 60-90 minutes before use.|
|(4) Remove dirts such as oil and dust from the groove.|
|Typical chemical composition of weld metal (%)|
|Typical mechanical properties of weld metal|
|Size & recommended current range (AC or DC+)|